PVDF
Polyvinylidene Fluoride
Polyvinylidene Fluoride (PVDF) Plate/rod Is A High-temperature Extruded Sheet And Rod Made Of Polyvinylidene Fluoride (PVDF). PVDF Has Good Chemical Inertia And Basically Does Not React With Any Medium. With High Temperature Resistance, High Temperature Resistance With Self-extinguishing, Especially Suitable For Pure Water Treatment System And The Transmission Of Pure Chemical Reagents In The Semiconductor Industry, The Use Of Temperature -60°C-150°C.
Advantage
Characteristic：
Excellent Chemical Corrosion Resistance And Hydrolysis Resistance, High Mechanical Strength, Good Wear Resistance And Sliding Properties, With Self-extinguishing, UV Resistance, Good Weather Resistance, Good Electrical Insulation.
Information
| Shape | Colour | |
 |  | |
| Plate | Bar | Natural Color |
| Thickness（mm） | Breadth（mm） | Length（mm） |
| 8-200 | 610 | 1220/2000 |
| Diameter（mm） | Length（mm） |
| 8-200 | 1000/2000 |
Specific gravit | ASTM D792 | g/cm3 | 1.75 |
Tensile yield strength | ASTM D638 | Mpa | 50 |
Breaking elongation | ASTM D638 | % | 10 |
Bending strength | ASTM D790 | Mpa | 80 |
Flexural modulus | ASTM D790 | Mpa | 2000 |
Shore hardness | ASTM D2240 | D | 78 |
Impact strength | ASTM D256 | J/M | 200 |
Melting point | DSC | °C | 175 |
Heat distortion temperature | ASTM D648 | °C | 140 |
Operating Temperature | - | °C | 150 |
Maximum operating temperature | - | °C | 180 |
Thermal conductivity | DIN 52612-1 | W/(K-M) | 0.13 |
Coefficient of linear themal | ASTM D696 | 10-5-1/K | 12 |
Dielectric strength | ASTM D150 | KV-mm | 22 |
Dielectric loss factor | ASTM D150 | - | 0.18 |
| Volume resistivit | ASTM D257 | Ω.cm | 1014 |
Surface resistivity | ASTM D257 | Ω | 1014 |
Dielectric constant | ASTM D149 | - | 7.25 |
| Water absorption | 23°C 60%RH | % | 0.1 |
Acid resistance | 23°C 60%RH | + | |
Alkali resistance | + | ||
Acid and alkali resistance | + | ||
Resistance to sodium chlorate | + | ||
Resistance to aromatic compounds | + | ||
Resistance to ketone | 23°C 60%RH | + | |
Resistance to hot water | 23°C 60%RH | + |
Flammability | UL 94 | V-0 | |
Viscosity | - | 0 | |
Non toxic | EEC 90/128 FDA | + | |
Coefficient of friction | DIN 53375 | 0.34 | |
Anti-ultraviolet | - | + |