Conductive PA

Polyamide

Relative to pure nylon material heat resistance, strength, stiffness. Creep resistance and dimensional stability, wear resistance and other properties have been improved, its maximum allowable temperature is higher, good aging resistance, mechanical vibration reduction ability is good.

Physical property table Physical property table download

Advantage

Characteristic：

Flame retardant V-0 grade, mechanical strength, stiffness, heat and wear resistance, creep resistance is good, with mechanical shock absorption performance, very suitable for automatic lathe machining.

Information

Shape		Colour

Plate	Bar	Black	Natural Color

Plate
Thickness（mm）	Breadth（mm）	Length（mm）
6-200	610/1000	1220/2000

Bar
Diameter（mm）	Length（mm）
6-200	1000/2000

Mechanical Properties

Specific gravit	ASTM D792	g/cm3	1.24
Tensile yield strength	ASTM D638	Mpa	55
Breaking elongation	ASTM D638	%	5
Bending strength	ASTM D790	Mpa	90
Flexural modulus	ASTM D790	Mpa	2200
Shore hardness	ASTM D2240	D	80
Impact strength	ASTM D256	J/M	45

Thermal Properties

Melting point	DSC	°C	240
Heat distortion temperature	ASTM D648	°C	90
Operating temperature	-	°C	105
Maximum operating temperature	-	°C	120
Thermal conductivity	DIN 52612-1	W/(K-M)	0.25
Coefficient of linear themal	ASTM D696	10-5-1/K	8

Electrical Properties

Dielectric strength	ASTM D150	KV-mm	-
Dielectric loss factor	ASTM D150	-	-
Volume resistivit	ASTM D257	Ω.cm	10^3-5
Surface resistivity	ASTM D257	Ω	10^3-5
Dielectric constant	ASTM D149	-	-

Chemical P roperties

Water absorption	23°C 60%RH	%	1.5
Acid resistance	23°C 60%RH		-
Alkali resistance			+
Acid and alkali resistance			+
Resistance to sodium chlorate			0
Resistance to aromatic compounds			+
Resistance to ketone	23°C 60%RH		+
Resistance to hot water	23°C 60%RH		+