PC+ABS

Polycarbonate

The alloy material modified by blending PC and ABS has better toughness and impact resistance than ABS, and still maintains good impact performance under low temperature, and the use temperature is -40-120°C

Physical property table Physical property table download

Advantage

Characteristic：

1.High mechanical strength, good creep resistance, high impact strength even at low temperatures; It has a rigid holding force in a large temperature range;

2.Resistance to energy rays, good electrical insulation, very good dimensional stability.

Information

Shape		Colour

Plate	Bar	Beige	Natural Color	Black

plate
Thickness（mm）	Breadth（mm）	Length（mm）
6-200	610	1220/2000

Bar
Diameter（mm）	Length（mm）
6-200	1000/2000

Mechanical Properties

Specific gravit	ASTM D792	g/cm3	1.13
Tensile yield strength	ASTM D638	Mpa	59
Breaking elongation	ASTM D638	%	54
Bending strength	ASTM D790	Mpa	65
Flexural modulus	ASTM D790	Mpa	2300
Shore hardness	ASTM D2240	D	84
Impact strength	ASTM D256	J/M	300

Thermal Properties

Melting point	DSC	°C	180
Heat distortion temperature	ASTM D648	°C	90
Operating temperature	-	°C	90
Maximum operating temperature	-	°C	120
Thermal conductivity	DIN 52612-1	W/(K-M)	0.17
Coefficient of linear themal	ASTM D696	10-5-1/K	9

Electrical Properties

Dielectric strength	ASTM D150	kv-mm	22
Dielectric loss factor	ASTM D150	-	0.015
Volume resistivit	ASTM D257	Ω.cm	10¹⁵
Surface resistivity	ASTM D257	Ω	10¹⁴
Dielectric constant	ASTM D149	-	3.3

Chemical P roperties

Water absorption	23°C 60%RH	%	0.4
Acid resistance	23°C 60%RH		+
Alkali resistance			0
Acid and alkali resistance			+
Resistance to sodium chlorate			0
Resistance to aromatic compounds			-
Resistance to ketone	23°C 60%RH		-
Resistance to hot water	23°C 60%RH		0