FR PC+ABS

Polycarbonate

PC+ABS is a PC+ABS based on the addition of flame retardants, to achieve a certain flame retardant effect of PC+ABS plastic, flame retardant grade up to UL94-V0. Operating temperature -40-120°C

Physical property table Physical property table download

Advantage

Characteristic：

High mechanical strength, good creep resistance, high impact strength even at low temperatures; It has a rigid holding force in a large temperature range; Energy ray resistance, good electrical insulation, very good dimensional stability, good flame retardant effect.

Information

Shape		Colour

Plate	Bar	Black	White

Plate
Thickness（mm）	Breadth（mm）	Length（mm）
6-200	610	1220/2000

Bar
Diameter（mm）	Length（mm）
6-200	1000/2000

Mechanical Properties

Specific gravit	ASTM D792	g/cm3	1.16
Tensile yield strength	ASTM D638	Mpa	60
Breaking elongation	ASTM D638	%	50
Bending strength	ASTM D790	Mpa	65
Flexural modulus	ASTM D790	Mpa	2300
Shore hardness	ASTM D2240	D	83
Impact strength	ASTM D256	J/M	260

Thermal Properties

Melting point	DSC	°C	180
Heat distortion temperature	ASTM D648	°C	90
Operating temperature	-	°C	90
Maximum operating temperature	-	°C	120
Thermal conductivity	DIN 52612-1	W/(K-M)	0.17
Coefficient of linear themal	ASTM D696	10-5-1/K	9

Electrical Properties

Dielectric strength	ASTM D150	kv-mm	22
Dielectric loss factor	ASTM D150	-	0.015
Volume resistivit	ASTM D257	Ω.cm	10¹⁵
Surface resistivity	ASTM D257	Ω	10¹⁴
Dielectric constant	ASTM D149	-	3.3

Chemical P roperties

Water absorption	23°C 60%RH	%	0.4
Acid resistance	23°C 60%RH		+
Alkali resistance			0
Acid and alkali resistance			+
Resistance to sodium chlorate			0
Resistance to aromatic compounds			-
Resistance to ketone	23°C 60%RH		-
Resistance to hot water	23°C 60%RH		0