ABS+PC

Acrylonitrile-butadiene-styrene

It is an alloy material modified by blending ABS and PC, which is better than ABS toughness and impact resistance, and still maintains good impact performance under low temperature, and the use temperature is -40-120°C.

Physical property table Physical property table download

Advantage

Characteristic：

Easy plating, coating, coloring, excellent impact resistance, heat resistance, low temperature resistance, chemical resistance and electrical properties, easy processing, dimensional stability.

Information

Shape		Colour

Plate	Bar	Black	Natural Color

plate
Thickness（mm）	Breadth（mm）	Length（mm）
6-100	610/1220	1220

Bar
Diameter（mm）	Length（mm）
6-150	1000

Mechanical Properties

Specific gravit	ASTM D792	g/cm3	1.13
Tensile yield strength	ASTM D638	Mpa	55
Breaking elongation	ASTM D638	%	11
Bending strength	ASTM D790	Mpa	80
Flexural modulus	ASTM D790	Mpa	2000
Shore hardness	ASTM D2240	D	82
Impact strength	ASTM D256	J/M	150

Thermal Properties

Melting point	DSC	°C	240
Heat distortion temperature	ASTM D648	°C	90
Operating temperature	-	°C	120
Maximum operating temperature	-	°C	145
Thermal conductivity	DIN 52612-1	W/(K-M)	0.5
Coefficient of linear themal	ASTM D696	10-5-1/K	8

Electrical Properties

Dielectric strength	ASTM D150	KV-mm	27
Dielectric loss factor	ASTM D150	-	0.009
Volume resistivit	ASTM D257	Ω.cm	10¹⁴
Surface resistivity	ASTM D257	Ω	10¹⁶
Dielectric constant	ASTM D149	-	25.2

Chemical P roperties

Water absorption	23°C 60%RH	%	0.6
Acid resistance	23°C 60%RH		-
Alkali resistance			+
Acid and alkali resistance			+
Resistance to sodium chlorate			0
Resistance to aromatic compounds			+
Resistance to ketone	23°C 60%RH		+
Resistance to hot water	23°C 60%RH		+